3D PRINTING

MAKING YOUR VISION REALITY

SLA IMAGE.png
SLA

Clear ABS Analogue

Tensile Strength : 50 - 56 MPa

Tensile Modulus : 2,700 - 2,920 MPa

Elongation at Break : 8% - 15%

Izod Impact, Notched : 2.05KJ/m²

HDT @0.45MPa : 49°C

sla boat.jpg
fdm

PLA (Polylactic Acid)

Tensile Strength(MPa): 62.63 Flexural Strength(MPa): 65.02 Impact Strength(MPa): 4.28 Melting Temperature°C: 190-220

ABS (Acrylonitrile Butadiene Styrene)

Tensile Strength(MPa): 40.96 Flexural Strength(MPa): 45.44 Impact Strength(MPa): 22.11 Melting Temperature°C: 220-260

fdm.png

Nylon

Tensile Strength(MPa): 50-55 Flexural Strength(MPa): 85-90 Impact Strength(MPa): 354 Melting Temperature°C: 220-260

sls
sls.png

Duraform Nylon PA

Tensile Strength(MPa): 43 Flexural Strength(MPa): 48 Impact Strength(MPa): 32 Hardness: 80 D

Nylon EX Black

Tensile Strength(MPa): 37 Flexural Strength(MPa): 15-17 Impact Strength(MPa): 32 Hardness: 74 D

Nylon GF 30% (Glass Fill)

Tensile Strength(MPa): 31 Flexural Strength(MPa): NA Impact Strength(MPa): 32 Hardness: NA

SLS.jpg

DIGITAL LIGHT PROJECTION

SELECTIVE LASER SINTERING

DLP

LS600

Tensile Modulus(MPa): 1,800 Tensile Strength (MPa):60 Elongation at Break: 4.39% Hardness (Shore D): 85 Izod Impact (Notched)(J/cm3): 0.63 Glass Transition Temperature (°C): 61 Appearance:Opaque yellow-beige Viscosity: 140 cP at 30° Density(cm3): 1.10 g

dlp image.png
Whatever your requirements are, we are always happy to help you achieve a solution that meets your needs and budget.